| 性能項目試驗條件[狀態(tài)]測試方法測試數(shù)據(jù)數(shù)據(jù)單位 |
| 基本性能熔體流動速率ASTM D123810g/10min |
| 熔體流動速率190℃/2.16kgISO 113310g/10min |
| 吸水率24 hrASTM D5700.2% |
| 物理性能比重ASTM D792,ISO 11831.42g/cm3 |
| 成型收縮率FlowASTM D955,ISO 294-41.8-2.2% |
| 成型收縮率Across FlowISO 294-41.8-2.2% |
| 洛氏硬度M-ScaleASTM D78594 |
| 洛氏硬度R-ScaleASTM D785120 |
| 機械性能拉伸模量ISO 527-23200MPa |
| 屈服拉伸應力ISO 527-272MPa |
| 拉伸應力ASTM D63869MPa |
| 斷裂伸長率ASTM D63860% |
| 斷裂伸長率ISO 527-250% |
| 彎曲模量ASTM D7902940MPa |
| 彎曲強度ASTM D790103MPa |
| 泰伯耐磨性1000 CyclesASTM D104413mg |
| charpy缺口沖擊強度23℃ISO 179/1eA10kJ/m2 |
| Izod 缺口沖強度ASTM D25678J/m |
| 熱性能熱變形溫度0.45MPa,unannealedASTM D648172℃ |
| 熱變形溫度0.45MPa,unannealedISO 75-2/B165℃ |
| 熱變形溫度1.8MPa,unannealedASTM D648136℃ |
| 熱變形溫度1.8MPa,unannealedISO 75-2/A100℃ |
| 流動方向線性熱膨脹系數(shù)ASTM E8310.0001cm/cm/℃ |
| 阻燃等級UL 94HB |