| 性能項目試驗條件[狀態(tài)]測試方法測試數(shù)據(jù)數(shù)據(jù)單位 |
| 基本性能比重ASTM D792, ISO 11831.42g/cm³ |
| 熔體質量流動速率ASTM D12382.8g/10 min |
| 熔體質量流動速率190℃/2.16kgISO 11332.8g/10 min |
| 成型收縮率flowASTM D955, ISO 294-41.8 to 2.2% |
| 成型收縮率Across flowISO 294-41.8 to 2.2% |
| 吸水率24hrASTM D5700.20% |
| 洛氏硬度M-ScaleASTM D78594 |
| 洛氏硬度R-ScaleASTM D785120 |
| 機械性能拉伸模量ISO 527-23100MPa |
| 拉伸應力YieldISO 527-271.0MPa |
| 拉伸應力ASTM D63868.0MPa |
| 拉伸伸長率BreakASTM D63875% |
| 拉伸伸長率BreakISO 527-265% |
| 彎曲模量ASTM D7902740MPa |
| 彎曲強度ASTM D79098.0MPa |
| 泰伯磨耗量1000次ASTM D104413.0mg |
| 夏比缺口沖擊強度23°CISO 179/1eA13kJ/m² |
| Izod缺口沖擊強度ASTM D256108J/m |
| 熱性能熱畸變溫度0.45MPa,未退火ASTM D648172°C |
| 熱畸變溫度1.8MPa,未退火ASTM D648133°C |
| 熱畸變溫度0.45MPa,未退火ISO 75-2/B163°C |
| 熱畸變溫度1.8MPa,未退火ISO 75-2/A96.0°C |
| 線性熱膨脹系數(shù)flowASTM E8310.00010cm/cm/°C |
| 其它性能阻燃等級UL 94HB |