| 性能項目試驗條件[狀態(tài)]測試方法測試數(shù)據(jù)數(shù)據(jù)單位 |
| 物理性能吸水均衡性50% RHL;DAMSimilar to ISO 622.6% |
| 粘性系數(shù)測試Viscosity Number;DAMISO 307275cm3/g |
| 吸水飽和性-DAMASTM D5708.5% |
| -DAMSimilar to ISO 628.5% |
| 密度-DAMASTM D7921.14g/cc |
| -DAMISO 11831.14g/cc |
| 線型模量收縮率橫向2.0mm;DAMISO 294-40.014cm/cm |
| 線型模量收縮率-Parallel;2.0mm;DAMISO 294-40.014cm/cm |
| -Flow;3.2mm(0.126in);DAMISO 294-40.015cm/cm |
| 吸水率immersion 24h;DAMASTM D5701.2% |
| 機械性能Charpy缺口沖擊-DAMISO 179/1eA0.6J/cm2 |
| -50% RHISO 179/1eA2J/cm2 |
| 低溫下charpy缺口沖擊--30℃；50% RHISO 179/1eU0.4J/cm2 |
| --30℃；DAMISO 179/1eU0.6J/cm2 |
| 拉伸屈服強度-50% RHISO 52755MPa |
| -50% RHASTM D63859MPa |
| -DAMISO 52783MPa |
| 彎曲模量-50% RHISO 1781.07GPa |
| -50% RHASTM D7901.21GPa |
| -DAMISO 1782.8GPa |
| -DAMASTM D7902.83GPa |
| 洛氏硬度-DAMASTM D78580M |
| -DAMASTM D785121R |
| 拉伸模量-50% RHISO 5271.3GPa |
| -DAMISO 5273.1GPa |
| 低溫下charpy抗沖擊強度--30℃；50% RHISO 179/1eUNB- |
| --30℃；DAMISO 179/1eUNB- |
| Charpy抗沖擊強度-50% RHISO 179/1eUNB- |
| -DAMISO 179/1eUNB- |
| IZOD沖擊-DAMASTM D2560.64J/cm |
| -50% RHASTM D2561.33J/cm |
| 拉伸率-50% RHASTM D63830% |
| -DAMISO 5274.4% |
| -DAMASTM D6385% |
| IZOD缺口沖擊-50% RHISO 180/1A23KJ/m2 |
| -DAMISO 180/1A6KJ/m2 |
| IZOD抗沖擊強度-DAMISO 180/1UNB- |
| -50% RHISO 180/1UNB- |
| 拉力抗沖強度Long specimen;DAMASTM D1822535KJ/m2 |
| 純強度-50% RHASTM D73263MPa |
| -DAMASTM D73266MPa |
| IZOD抗沖-50% RHASTM D2560.27J/cm |
| -DAMASTM D2560.32J/cm |
| 拉伸強度-50% RHASTM D63877MPa |
| -DAMASTM D63885MPa |
| 電氣性能體積電阻率-50% RHIEC 600931e+011ohm-cm |
| -DAMIEC 600931e+013ohm-cm |
| 介電常數(shù)-1MHz;50%RHIEC 602504.2- |
| -100Hz;DAMIEC 602504.3- |
| -50%RHASTM D1504.6- |
| -50%RHASTM D1507- |
| -50%RHASTM D1508- |
| 介電常數(shù)-100Hz;50%RHIEC 6025010.03- |
| -DAMASTM D1503.6- |
| -MHz;DAMIEC 602503.6- |
| -DAMASTM D1503.9- |
| -DAMASTM D1504- |
| 介電損耗因素-100Hz;DAMASTM D1500.01- |
| -100Hz;DAMIEC 602500.015- |
| -1KHz;DAMASTM D1500.02- |
| -1MHz;DAMASTM D1500.02- |
| 加工性能熔融溫度DAM280-300℃ |
| 干燥損失率DAMMax0.05% |
| 模量溫度DAM50-90℃ |
| 熱性能ULRTI，機械性-3.0mm;DAMUL 746B85℃ |
| -1.5MM;DAMUL 746B85℃ |
| 熱膨脹系數(shù)線型20℃下橫流23-55℃(73-130°F);DAMASTM E831100μm/m-℃ |
| 線型20℃下橫流23-55℃(73-130°F);DAMISO 11359-1/-2100μm/m-℃ |
| ULRTI，電氣性-3.0mm;DAMUL 746B125℃ |
| -1.5MM;DAMUL 746B125℃ |
| 氧氣指數(shù)DAMISO 4589-1/-228% |
| 脆化溫度DAMASTM D746-100℃ |
| 熔點-10℃/min;DAMISO 11357-1-3262℃ |
| -DAMASTM D3418263℃ |
| 變形溫度-at 0.46 MPaISO 75-1/-2200℃ |
| -at 0.46 MPaASTM D648210℃ |
| -at 1.8 MPaASTM D64865℃ |
| -at 1.8 MPaISO 75-1/-270℃ |
| 燃燒性-1.5mm;DAMUL 94HB- |
| -1.5mm;DAMIEC 60695-11-10HB- |
| -0.71mm;DAMIEC 60695-11-10HB- |
| -0.71mm;DAMUL 94HB- |
| -3.0mm;DAMIEC 60695-11-10HB- |
| -3.0mm;DAMUL 94HB- |
| 熱膨脹系數(shù)線型20℃Parallel;23-55℃(73-130°F);DAMASTM E831100μm/m-℃ |
| 線型20℃Parallel;23-55℃(73-130°F);DAMISO 11359-1/-2100μm/m-℃ |
| ULRTI,抗沖性機械性能-1.5mm;DAMUL 746B75℃ |
| -3.0mm;DAMUL 746B75℃ |
| 其它性能顏色天然 |
| 形式粒子 |
| 加工方法---注塑成型- |
| ---擠出- |
| ---注塑- |
| ---涂層- |