| Density |
1.21g/cc |
0.0437lb/in³ |
| Linear Mold Shrinkage, Flow |
0.00200-0.00600cm/cm
@Thickness 3.20 mm |
0.00200-0.00600in/in
@Thickness 0.126 in |
| |
Mechanical Properties
Metric
English
Comments
| Tensile Strength, Yield |
36.0MPa |
5220psi |
| Elongation at Break |
36.0 % |
36.0 % |
| Elongation at Yield |
4.00 % |
4.00 % |
| Tensile Modulus |
1.66GPa |
241ksi |
| Charpy Impact Unnotched |
NB |
NB |
|
NB
@Temperature -30.0 °C |
NB
@Temperature -22.0 °F |
| Charpy Impact, Notched |
1.82J/cm² |
8.66ft-lb/in² |
|
0.850J/cm²
@Temperature -30.0 °C |
4.05ft-lb/in²
@Temperature -22.0 °F |
| |
Thermal Properties
Metric
English
Comments
| CTE, linear |
88.0µm/m-°C
@Temperature 20.0 °C |
48.9µin/in-°F
@Temperature 68.0 °F |
| CTE, linear, Transverse to Flow |
140µm/m-°C
@Temperature 20.0 °C |
77.8µin/in-°F
@Temperature 68.0 °F |
| Deflection Temperature at 0.46 MPa (66 psi) |
94.0°C |
201°F |
| Deflection Temperature at 1.8 MPa (264 psi) |
86.0°C |
187°F |
| Vicat Softening Point |
91.0°C |
196°F |
| Glass Transition Temp, Tg |
104°C |
219° |